Notched Chocky Bar 240 x 50 x 23mm CB50

Specification:
Part No. CB50  / CB-50
Weight    1.9  Kg
Brand Name   OEM AVAIABLE
Type: Chocky Bar
Machine Type: BUCKETS / EXCAVATORS / CRUSHER

 

REQUEST FOR PARTS QUOTE

Notched Chocky Bar 240 x 50 x 23mm CB50 for All Earth-Moving Machinery & Equipment, DOMITE Cast Alloy 700BHN High Chromium Chocky Bars, Laminated  ASTM A532 15/3CrMo Wear Chocky Bar, 700 brunell high chromium white iron chocky bar with a mild steel weldable backing plate, Bimetallic Wear Resistant Chocky Bars Chocky Blocks, bucket wear solutions for earthmoving machines, construction & mining equipment CRUSHER Excavator Loader Dozer

Notched Chocky Bar 240 x 50 x 23mm CB50  Detail Information
Applicable Industries:Energy & Mining
Type:Chocky Bar CB50
Machine Type: BUCKETS / EXCAVATORS / CRUSHER
Material:Chromium
Processing Type: Casting
Use:ORE MINING & COAL MINING & EARTHMOVING
Hardness:63HRC
Shearing Strength:210Mpa Min
Impact Toughness:Up To 150J/cm2
Color:Black
Size:240*50*23mm

23mm x 50mm x 240mm White iron chocky bar popularly known as CB50 chocky bar. Used as effective protection for sliding abrasion in areas of high wear.Applications include to fixed and mobile plant situations.This is an excellent solution for those areas of high wear that are causing problems for customers, this part can be easily formed and welded onto curved or flat surfaces. This product is ideal for use on loader and excavator buckets for earth moving machinery, but is also useful for areas of high wear in many industries such as recycling, quarrying, & demolition etc.This size is just one of a number of different sizes and shapes that are available.

Applications of Chocky Bars are widely varied, ranging from specific wear protection on buckets for loaders, excavators and dragline machines, or for weld-on hammer tips for recycling industry, or chute linings and rock box edges.
They are easy to use and install. They can be bent, cut and formed to suit different surfaces.

Laminated White Iron Wear Blocks combined very high wear resistant qualities of a high chrome cast iron (15/3CrMo, 700 BHN – 63 HRc) with a weldable & high impact toughness mild steel by Vacuum brazing furnace, which are exceptionally resistant to impact and abrasion while retaining.
Both high abrasion resistance and high impact toughness !

Design Features
White Iron
Vacuumed brazed and liquid nitrogen cooled to achieve a high strength joint
Mild steel backing offers strength, machinability, and impact resistance
Can be welded in place, through-bolted, stud bolted, drilled, tapped, keyed.
Ease if fitment, very versatile
Lower operating costs
Longer Service when compared to conventional materials
Increased production
Improved product efficiency
Increased equipment availability

Combination of high chromium and molybdenum white iron metallurgically bonded to a mild steel plate. provides maximum protection in high wear areas, with the mild steel backing cushioning the white iron enabling it to withstand impact. Wear Resistant Products Bucket Protection Chocky Bar CB50  is easily weldable to areas of the conveyor system with minimal preparation providing unsurpassed resistance to abrasive bulk material wear. Excavator Bcuket Wear Parts CB65 Chocky Bar

Item No.
Size
(mm)
Dimension (mm)
N.W. 
(kg)
A
B
C
D
CB 25
240×25×23
240
25
15
23
0.9
CB 40
240×40×23
240
40
15
23
1.5
CB 50
240×50×23
240
50
15
23
1.9
CB 65
240×65×23
240
65
15
23
2.5
CB 80
240×80×23
240
80
15
23
3.2
CB 90
240×90×23
240
90
15
23
3.5
CB 100
240×100×23
240
100
15
23
3.9
CB 130
240×130×23
240
130
15
23
5.4
CB 150
240×150×23
240
150
15
23
6.0